本型号主要用于：水管配件 / 汽车前后扰流板 / 摩托车挡板 / 押出水管 / 安全帽 / 滤水器外壳
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 熔体流动速率 | 200℃5kg | ASTM D-1238 | 0.6 | g/10min |
| 比重 | | ASTM D-792 | 1.03 | 23/23℃ |
| 燃烧率 | File No. E56070 ULC-UL | | 1/16HB |
| 熔体流动速率 | 220℃10kg | ASTM D-1238 | 6 | g/10min |
| 弯曲强度 | | ASTM D-790 | 9070 | lb/in2 |
| 弯曲强度 | | ASTM D-790 | 640 | kg/cm2 |
| 弯曲弹性率 | | ASTM D-790 | 3.2105 | lb/in2 |
| IZOD冲击强度 | 1/4 | ASTM D-256 | 40 | kg.cm/cm |
| IZOD冲击强度 | 1/8 | ASTM D-256 | 45 | kg.cm/cm |
| 洛氏硬度 | | ASTM D-785 | 102 | R |
| IZOD冲击强度 | 1/4 | ASTM D-256 | 7.4 | ft.lb/in |
| 引张强度 | | ASTM D-638 | 400 | kg/cm2 |
| IZOD冲击强度 | 1/8 | ASTM D-256 | 8.4 | ft.lb/in |
| 伸长率 | | ASTM D-638 | 40 | % |
| 引张强度 | | ASTM D-638 | 5670 | lb/in2 |
| 弯曲弹性率 | | ASTM D-790 | 2.3104 | kg/cm2 |
| 维卡软化点 | | ASTM D-1525 | 105 | ℃ |
| 维卡软化点 | | ASTM D-1525 | 221 | ℉ |
| 热变形温度 | | ASTM D-648 | 88(190) | ℉ |
| 热变形温度 | | ASTM D-648 | 98(208) | ℃ |
POLYLAC®ABS
ABS由苯乙烯、丙烯腈和丁二烯乳浆共聚合而成，本身耐热性和耐溶剂性均比HIPS为佳，且具有光泽性。由于丙烯腈的腈基极性较强，可以增强PS中分子链的相互作用，所以冲击强度、拉伸强度及塑件的表面硬度均较HIPS为佳。一般丙烯腈的比例含量愈高，其耐热性、刚性及耐溶剂性愈佳，但流动性愈差且塑料底色带黄，在注射成形(Injection Mold)时其机械性及尺寸安定性非常好，基于上述的优点ABS树脂成为一种优秀的工程塑料。
奇美的POLYLAC®ABS树脂是现今市场上最多样化的丙烯腈一丁二烯一苯乙烯共聚合物，我们独特的技术，促使ABS树脂在强度、安定性、加工性上有其特殊的搭配组合，奇美POLYLAC®的质量、染色性及外观，深受顾客之信赖及喜好。POLYLAC®已被广泛接受而应用于商业机械、电子零件、通讯设施、个人计算机、电气器具、汽车零件、淋浴用具、行李箱、水龙头及其他家居用品。POLYLAC®涵盖市场上之各种不同规格，且经UL和C-UL认证合格，一般级、高流动级、押出级、防火级及耐热级等规格，可实时稳定供货。另外，亦配合新用途开发新品级，以开拓新市场。